MarinaQuadro BWP
A marine-grade plywood complying with E0 emission norms, emitting negligible amounts of formaldehyde, making your interiors a safe space. Our VierPro technology with 4 steps of Hot and Cold pressing lends uniformity and is compressed to give extra strength. Being Marine BWP grade ply it is naturally immune to termite attacks, borer, and fungus . Backed by a solid 30-year warranty, MarinaQuadro is the most preferred plywood, and can be used for making best-in-class and long-enduring furniture, modular kitchen cabinets.
Thickness (MM)
Sizes (MM)
Application
Borer & Termite Proof
Boiling Waterproof
Matt Ply
IS 710
Fully Calibrated
VierPro Technology
30 Years Warranty
E-0 Emission Level
PF - Glue Line Protection
Premium Gurjan Face
| SR NO. | Tests Method | ISI Requirements | Observed Values |
|---|---|---|---|
| 1 | Dimension Squareness | Length :+ 6mm Width :+ 3mm Thicknes :+/- 5% Max : 0.20% |
Length- 2442 mm Width- 1221 mm Thickness- 19 mm Squareness - 0.16% |
| 2 | Moisture content | Moisture content should not be less than 5% and not more than 15% | 7.65% |
| 3 | Glue Adhesion in Dry State (a) Glue Shear Strength |
Avg.: 1350 N Min. Individual: Avg.: 1100 N |
1411 N 1176 N |
| (b) Adhesion of Plies | Bond shall show minimum Pass Standard, Poor or Excellent |
Satisfactory | |
| 4 | Water Resistance Test (After 72 Hours boiling in water) (a) Glue Shear Strength |
Average : 1000 N Minimum Individual : 800 N |
1249 N 915 N |
| (b) Adhesion of Plies | Bond shall show minimum Pass Standard, Poor or Excellent |
Satisfactory | |
| 5 | Tensile Strength (a) Along the grain direction |
Should not be less than 42.0 N/mm² |
54.20 N/mm² |
| (b)Across the grain direction | Should not be less than 25.0 N/mm² | 41.82 N/mm² | |
| (c) Sum of both the direction | Should not bf less than 84.5 N/mm² | 96.02 N/mm² | |
| 6 | Mycological Test (a) Glue Shear Strength |
Average 1000 N Minimum lndividual : 800 N |
1250 N 1010 N |
| (b) Adhesion of Plies | Adherent fibre distributed more or less uniformly | Excellent | |
| 7 | STATIC BENDING STRENGTH ( DRY STATE ) | ||
| Modulus of Elasticity (a) Along the grains of the face Veneer |
Average: 7500 N/mm² Min. lndividual-6700 N/mm² |
7950 N/mm² 7270 N/mm² |
|
| b) Across the grain of the Face Veneer | Average: 4000 N/mm² Min. lndividual-3600 N/mm² |
4845 N/mm² 4115 N/mm² |
|
| Modulus of Rupture (a) Along the grains of the face Veneer |
Average: 50 N/mm² Min. lndividual-45 N/mm² |
60 N/mm² 55 N/mm² |
|
| (b) Across the grain of the Face Veneer | Average: 30 N/mm² Min. lndividual-27 N/mm² |
36 N/mm² 29 N/mm² |
|
| 8 | STATIC BENDING STRENGTH ( WET STATE ) | ||
| Modulus of Elasticity (a) Along the grains of the face Veneer |
Average: 3570 N/mm² Min. lndividual- 3400 N/mm² |
4525 N/mm² 3770 N/mm² |
|
| b) Across the grains of the Face Veener | Average: 2000 N/mm² Min. lndividual-1800 N/mm² |
2845 N/mm² 2215 N/mm² |
|
| Modulus of Rupture (a) Along the grains of the face Veneer |
Average: 25 N/mm² Min. lndividual-22 N/mm² |
30 N/mm² 25 N/mm² |
|
| (b) Across the grains of the Face Veener | Average: 15 N/mm² Min. lndividual-13 |
21 N/mm² 15 N/mm² |
|